Comparison of Properties with Relevance for the Automotive Sector in Mechanically Recycled and Virgin Polypropylene

Polypropylene (PP) has a high recycling potential. However, the properties of mechanically recycled PP (R-PP) have not been fully compared to those of virgin PP (V-PP). Therefore, in this study, properties of R-PP and V-PP were compared using data from recyclers, virgin plastic suppliers, and the literature. The properties of recyclates could not be directly correlated either with the properties of the virgin polymers from which the recyclates were made or the recycling parameters. It was found that the MFR of R-PP was higher; MFR R-PP had a median value (m) of 11 g/10 min while MFR V-PP had a median value of 6.3 g/10 min (at 230 °C and with 2.16 kg). In terms of mechanical properties, in many cases R-PP exhibited stiffer and more brittle behavior, with a slightly higher Young's modulus (ER-PP = 1400 and EV-PP = 1200 MPa), a reduced elongation at break (ɛbR-PP = 4 l.-% and ɛbV-PP = 83 l.-%), and notched charpy impact strength (NCISR-PP = 4.8 and NCISV-PP = 7.5 kJ/m2). However, the values for every property had a broad distribution. In addition to existing information from the literature, our research sheds fresh light on the variation of the characteristics of recycled polypropylenes presently on the market.