  4. Analysis of structural and functional properties of Ni50Mn30Ga20 after plastic deformation
 
  • Details
  • Full
Options
2006
Conference Paper
Titel

Analysis of structural and functional properties of Ni50Mn30Ga20 after plastic deformation

Abstract
Some NiMnGa single crystals exhibit a magnetic-field-induced strain (MFIS) in the low temperature martensitic phase. In order to obtain such MFIS in polycrystalline samples, the use of textured samples is most promising. The paper describes experimental results of compression tests of a Ni50Mn30Ga20 alloy at high temperatures up to 1000 °C which show that the magnetic shape memory alloy (MSMA) exhibits a good plastic deformation behavior above the ordering temperature in the B2 (CsCl) structure. Flow curves were obtained for various strain rates. Experiments using the hot rolling process were successful. The results show that it is possible to obtain pre-orientation of the twinned martensitic structure. The cast and hot-rolled specimens were characterized by differential scanning calorimetry, X-ray diffraction and optical microscopy using differential interference contrast. The changes in structural properties of specimens after plastic deformation are presented and discussed.

; 

Some NiMnGa single crystals exhibit a magnetic-field-induced strain (MFIS) in the low temperature martensitic phase. In order to obtain such MFIS in polycrystalline samples, the use of textured samples is most promising. The paper describes experimental results of compression tests of a Ni50Mn30Ga20 alloy at high temperatures up to 1000 °C which show that the magnetic shape memory alloy (MSMA) exhibits a good plastic deformation behavior above the ordering temperature in the B2 (CsCl) structure. Flow curves were obtained for various strain rates. Experiments using the hot rolling process were successful. The results show that it is possible to obtain pre-orientation of the twinned martensitic structure. The cast and hot-rolled specimens were characterized by differential scanning calorimetry, X-ray diffraction and optical microscopy using differential interference contrast. The changes in structural properties of specimens after plastic deformation are presented and discussed.
Author(s)
Böhm, A.
Naumann, G.
Drossel, W.-G.
Neugebauer, Reimund
Hauptwerk
7th European Symposium on Martensitic Transformations and Shape Memory Alloys 2006
Konferenz
European Symposium on Martensitic Transformations (ESOMAT) 2006
Thumbnail Image
Language
English
google-scholar
Fraunhofer-Institut für Werkzeugmaschinen und Umformtechnik IWU
Tags
  • shape memory alloy

  • NiMnGa

  • martensitic transform...