Bodkin, R.R.BodkinHerrmann, M.M.HerrmannCoville-Neil, J.J.Coville-NeilSigalas, I.I.Sigalas2022-03-042022-03-042009https://publica.fraunhofer.de/handle/publica/21886710.3139/146.110082The Al(x)Mg(1-x)B2 solid solution was studied at temperatures of 900, 1000, 1200 and 1400 C using X-ray diffraction. From the obtained data, isothermal sections at 1000, 1200 and 1400 deg C have been proposed for the Al-Mg-B ternary system. Based on these results there exists an equilibrium between Al and AlMgB14 at temperatures above 1000 deg C. Entnommen aus <a_href="http://www.fiz-technik.de/db/b_tema.htm" target="_blank">TEMA</a>en620666669journal article