Prodi-Schwab, A.A.Prodi-SchwabLuthge, T.T.LuthgeJahn, R.R.JahnHerbig, B.B.HerbigLobmann, P.P.Lobmann2022-03-042022-03-042008https://publica.fraunhofer.de/handle/publica/21583710.1007/s10971-008-1749-5Dispersions of crystalline nanoscaled ITO and solutions of amorphous precursors were used for the preparation of transparent conductive films on glass both by large area dip-coating (30 x 30 cm(2)) and pad-printing. The advantages of both types of coating materials regarding single layer thickness and conductivity were combined by a coating-infiltration procedure. The resulting films showed a specific resistivity down to 1.77 10E-03 Omega cm after treatment in reducing atmosphere and an increased resistance to subsequent storage in air.en666620journal article