Preußner, JohannesJohannesPreußnerRödler, GeorgGeorgRödlerFischer, Felix GabrielFelix GabrielFischerHintz, KarinKarinHintzFriedmann, ValerieValerieFriedmannWeisheit, AndreasAndreasWeisheit2023-11-222024-02-192023-11-222023https://publica.fraunhofer.de/handle/publica/45715310.1515/pm-2023-0062High strength and low density materials are needed to achieve lightweight design of components. Aluminum base metals alloyed with calcium are of potential interest because of the low density of calcium and its abundance. The additive manufacturing of dense and crack free samples out of an Al-10 wt.% Ca (Al-10Ca) alloy is presented. Both laser-based direct energy deposition (DED-LB) and laser powder bed fusion (LPBF) processes were applied to manufacture sample material. Preheating of the substrate plate is needed in LPBF to receive crack free samples. An analysis of the microstructure shows an Al-Al4Ca lamellar eutectic.Zur Herstellung von Bauteilen in Leichtbauwei se werden Werkstoffe mit hoher Festigkeit und geringer Dichte benötigt. Mit Calcium legierte Metalle auf Aluminiumbasis sind aufgrund der geringen Dichte und der großen Verfügbarkeit des Calciums von potenziellem Interesse. Vor gestellt wird die additive Fertigung dichter und rissfreier Proben aus einer Al-10 Gew. % Ca Legierung (Al-10 Ca). Zur Herstellung des Pro benmaterials kam sowohl das pulverbasierte Laserauftragschweißen (laser based direct energy deposition (DED-LB)) als auch das pul verbettbasierte Laserstrahlschmelzen (engl. Laser Powder Bed Fusion, LPBF) zum Einsatz. Im Fall der LPBF muss die Substratplatte zur Gewährleistung rissfreier Proben vorgewärmt werden. Die Gefügeanalyse ergibt ein lamella res Al-Al4Ca-Eutektikum.enaluminiumaluminumcalciumDEDLPBFmicrostructurejournal article