Phase-field simulation of the dendrite fragmentation by electromagnetic stirring in AA5754 aluminum alloy laser beam welding

A phase-field model including magnetic field induced dendrite fragmentation was established and applied to the cases with different initial crystal nuclear positions for AA5754 aluminum alloy electromagnetic laser beam welding. Compare the calculated results that include dendrite fragmentation caused by the thermal electromagnetic Lorentz force with the results that consider only the thermal electromagnetic Lorentz force, without fragmentation, at the characteristic time instants. Both in the early and late stages, the small fragmentation at the dendrite tip promotes the number of higher-order branches and their growth, especially in the direction perpendicular to the solidification. The later stage fragmentation has the possibility of breaking one grain into several, which verifies the possibility of grain refinement caused by dendrite fragmentation. The fracture surface caused by fragmentation also makes more solid-liquid interfaces and their growth. In addition, the cases with different initial nuclear positions were compared. The grain growth in the low-temperature zone can be inhibited by the equiaxed grains' fragmentation at the high-temperature area (179.8 μm and 14.7 % start at the center, 115.4 μm and 9.4 % start at the high-temperature corner, 134.3 μm and 10.9 % start at the low-temperature corner), which is another kind of grain refinement by the dendrite fragmentation. This kind of inhibition effect on grain growth in the low-temperature region will be enhanced with the increasing time interval between the two crystal nuclei' appearance (179.8 μm and 14.7 % when virtual grains appear at t = 4.3803 s and t = 4.3803 s, 134.3 μm and 10.9 % at t = 4.0977 s and t = 3.9564 s, and 115.4 μm and 9.4 % at t = 3.8151 s and t = 3.5325 s).