  4. Tribological and hydrothermal behaviour of silicon carbide under water lubrication
 
  • Details
  • Full
Options
2009
Journal Article
Title

Tribological and hydrothermal behaviour of silicon carbide under water lubrication

Abstract
In this study the tribological and hydrothermal behaviour of silicon carbide was examined. No significant reaction layer was found after tribochemical experiments conducted on sintered silicon carbide (SSiC) and after hydrothermal treatment using a hydrothermal diamond anvil cell (HDAC). Mechanical contact of sliding parts induced superficial amorphisation and chemical analysis showed a slight increase in oxygen content within the topmost part of the surface. Static experiments using single-crystal silicon carbide (SCSiC) and a hydrothermal diamond anvil cell revealed an active oxidation mechanism and silica as the result of solution and precipitation.
Author(s)
Presser, V.
Krummhauer, O.
Nickel, K.G.
Kailer, A.
Berthold, C.
Raisch, C.
Journal
Wear  
DOI
10.1016/j.wear.2008.10.001
Language
English
Fraunhofer-Institut für Werkstoffmechanik IWM  
Keyword(s)
  • tribochemistry

  • corrosion

  • modelling

  • silicon carbide

  • hydrothermal