A planar copolymer for high efficiency polymer solar cells

An alternating copolymer, poly(2-(5-(5,6-bis(octyloxy)-4-(thiophen-2-yl)benzo[c][1,2,5]thiadiazol- 7-yl)thiophen-2-yl)-9-octyt-9H-carbazole) (HXS-1), was designed, synthesized, and used as the donor material for high efficiency polymer solar cells. The close packing of the polymer chains in the solid state was confirmed by XRD. A J(sc) of 9.6 mA/cm(2), a V-proportional to of 0.81 V, an FF of 0.69, and a PCE of 5.4% were achieved with HXS-1 and [6,6]-phenyl C-71-butyric acid methyl ester (PC71BM) as a bulk heterojunction active layer spin-coated from a solvent mixture of 1,2-dichlorobenzene and 1,8-diodooctane (97.5:2.5) under air mass 1.5 global (AM 1.5 G) irradiation of 100 mW/cm(2).