Comparative Studies of the Structural and Physicochemical Properties of the First Fullerene Derivative FD-C60 (Fullerenol) and Second Fullerene Derivate SD-C60 (3HFWC)
Abstract
In order to maximally reduce the toxicity of fullerenol (the first derivative of C60, FD-C60), and increase its biomedical efficiency, the second derivative SD-C60 (3HFWC, Hyper-Harmonized Hydroxylated Fullerene Water Complex) was created. Several different methods were applied in the comparative characterization of FD-C60 and SD-C60 with the same OH groups in their core. FD-C60 as an individual structure was about 1.3 nm in size, while SD-C60 as an individual structure was 10-30 nm in size. Based on ten physicochemical methods and techniques, FD-C60 and SD-C60 were found to be two different substances in terms of size, structure, and physicochemical properties; FD-C60, at 100 °C, had endothermic characteristics, while SD-C60, at 133 °C, had exothermic characteristics; FD-C60 did not have water layers, while SD-C60 had water layers; the zeta potential of FD-C60 was -25.85 mV, while it was -43.29 mV for SD-C60. SD-C60 is a promising substance for use in cosmetics and pharmaceuticals.
Author(s)
Koruga, Djuro
NanoLab, Department of Biomedical Engineering, Faculty of Mechanical Engineering, University of Belgrade, Belgrade, Serbia
Stanković, Ivana
NanoLab, Department of Biomedical Engineering, Faculty of Mechanical Engineering, University of Belgrade, Belgrade, Serbia
Matija, Lidija
NanoLab, Department of Biomedical Engineering, Faculty of Mechanical Engineering, University of Belgrade, Belgrade, Serbia