Uhlmann, EckartEckartUhlmannBolz, RobertRobertBolzPolte, MitchelMitchelPolteBörnstein, JulianJulianBörnstein2023-07-102023-07-102022https://publica.fraunhofer.de/handle/publica/44534610.1016/j.procir.2022.09.1362-s2.0-85143896763In sinking electrical discharge machining (EDM), tool electrode wear is crucial for an economical production. The tool electrode wear affects the process efficiency and determines the number of required tool electrodes for a specific machining process. Therefore, the relative tool wear, describing the relation of removed material volume between tool and workpiece electrode, needs to be minimised. The tool wear characteristics in sinking EDM depend strongly on EDM processing parameters and the applied electrode materials. Especially in micro-EDM, a significant increase of relative tool wear is representative. Because of its thermophysical properties tungsten carbide-cobalt (WC-Co) is a suitable material for the application as sinking EDM tool electrode. The economical production of WC-Co form electrodes for EDM sinking is enabled by recent advancements in precision milling of hard materials. Due to non-existent research on which composition of WC-Co is most advantageous for the application as sinking EDM tool electrode material, previous investigations have been intensified to describe correlations between material properties, EDM processing parameters and EDM processing results concerning material removal rate and relative tool wear. Therefore, various WC-Co grades with differing grain size and cobalt content were analysed in sinking EDM experimental studies. It was observed that the factor grain size showed an ambiguous effect concerning the process results. An increasing cobalt content led to a reduction of relative tool wear, which can be explained by the microstructure of the cobalt binder phase with its higher electrical conductivity. The WC-Co grades with beneficial EDM processing results have been further investigated in EDM parameter studies with differing tool electrode geometries. The experimental results concerning relative tool wear, with a minimum of 3 % for macro- and 5 % for micro-sized geometries, proved the suitability of specific WC-Co compositions as tool electrode material for sinking EDM.enEDMelectrical discharge machiningrelative tool weartungsten carbide-cobaltjournal article