Herrmann, M.M.HerrmannBalzer, B.B.BalzerSchubert, C.C.SchubertHermel, W.W.Hermel2022-03-032022-03-031993https://publica.fraunhofer.de/handle/publica/18272910.1016/0955-2219(93)90104-YDense Si3N4-TiN-composites with 20 - 50 wt-percent TiN with various grain sizes were produced by hot pressing and gas-pressure sintering under nitrogen gas atmosphere. The dependence of the densification behaviour on the TiN-content and on the grain size of TiN was investigated. Starting from the thermodynamical considerations the influence of the C- content in the Ti(C,N) on the densification was analysed and tested by experiment.enEigenschaftKompositeparticle-reinforced compositePartikelverstärkungpropertySi3N4Siliciumnitridsilicon nitridesinteringSinternTiNtitanium nitrideTitannitrid666620journal article