Erhard, PatriciaPatriciaErhardSeidel, A.A.SeidelVogt, JoachimJoachimVogtVolk, W.W.VolkGünther, D.D.Günther2022-03-062022-03-062022https://publica.fraunhofer.de/handle/publica/27063410.1007/s11740-021-01078-8Slurry-based 3D printing allows ceramic green bodies to be fabricated at high packing densities. In contrast to powder-based binder jetting, full densification of printed parts can be achieved in a subsequent sintering step as fine particles dispersed in a suspension are cast and compacted. Slurry-based 3D printing is thus expected to overcome the application limits of the powder-based alternative in metal casting in terms of unfavorable properties like high surface roughness, low density and low mechanical strength. To ensure stress-free drying and therefore high qualities of the compounds made in layers, it is crucial to fabricate single layers with a high level of homogeneity. This paper presents a CFD model based on the open-source simulation environment OpenFOAM to predict the resulting homogeneity of a cast slurry layer with defined parameter sets or coater geometries using the Volume-Of-Fluid method. Moreover, a novel method of spatial reconstruction is proposed to evaluate the surface quality of layers on a minimised computional demand. By comparing the results of the simulation with the real macroscopic behaviour determined in experiments, the approach is found to be a useful tool for suggesting suitable parameters and coater geometries for processing slurries. A precise reconstruction of the outline of the coating area with different process parameters and an approximate prediction of the effect on surface roughness was achieved.enadditive manufacturing3D printingceramicslurry castingCFDSimulationmultiphaseVOFspatial reconstruction666658journal article