Wang, DongxiangDongxiangWangHauptmann, JacquelineJacquelineHauptmannMay, ChristianChristianMayHofstetter, Yvonne JasminYvonne JasminHofstetterVaynzof, YanaYanaVaynzofMüller, TobiasTobiasMüller2022-03-062022-03-062021https://publica.fraunhofer.de/handle/publica/26665810.1088/2058-8585/abf159Transparency and bendability are some of the most attractive unique selling points for OLED lighting, enabling a variety of new application possibilities for industrial and private end-users. The roll-to-roll (R2R) OLED fabrication based on thermal evaporation offers a fast, continuous-running solution for producing flexible OLEDs at a lower cost. In this work, R2R fabricated large-area highly transparent thermal co-evaporated Ca:Ag (2:1 vol.%) top-electrode with mean transmittance of 64% over the visible range and a corresponding sheet resistance of as low as 21 Ohm/sq was achieved. By increasing the film thickness to 24 nm, the sheet resistance can be further reduced to 12 Ohm/sq, albeit with a lower mean transmittance of 58%. The Ca:Ag electrode demonstrates a high mechanical durability through 1000 bending cycles, which is highly desirable as a characteristic for flexible electronics, as well as for the R2R fabrication. Finally, the stability of the Ca:Ag electrode in vacuum and ambient was studied as well.enflexible OLEDhighly transparent electrodeR2R fabricationco-evaporationUltrathin Glass620667670journal article