Müller, RalphRalphMüllerReichel, ChristianChristianReichelSchrof, J.J.SchrofPadilla, MilanMilanPadillaSelinger, M.M.SelingerGeisemeyer, InoInoGeisemeyerBenick, JanJanBenickHermle, MartinMartinHermle2022-03-052022-03-052015https://publica.fraunhofer.de/handle/publica/24035810.1016/j.solmat.2015.05.046Interdigitated back-contact (IBC) solar cells were fabricated with a process sequence combining local ion implantation of phosphorus and full area BBr3 furnace diffusion resulting in conversion efficiencies of up to 22.4%. The highly doped emitter and BSF are in direct contact to each other (p+n+ junction) leading to a controlled junction breakdown at low reverse-bias voltages of around 5 V. The breakdown was located at the p+n+ junction and found to be homogeneously distributed over the whole cell area. This is not critical for module integration as the absolute temperature rise of a reverse-biased cell was determined to be less than 35 K. After reverse breakdown, the conversion efficiency degraded by 1-2% absolute due to additional recombination at the p+n+ junction. The cell performance could be fully recovered by a short annealing at 300 °C indicating that the Al2O3 passivation was altered by the reverse breakdown. This might be a fundamental issue for Al2O3 passivated IBC solar cells without gap between emitter and BSF, independent from the doping method.enSolarzellen - Entwicklung und CharakterisierungSilicium-PhotovoltaikHerstellung und Analyse von hocheffizienten Solarzellen621journal article