Under CopyrightHohe, JörgWood, Jeffrey T.Gumbsch, PeterRohrmüller, BenediktBenediktRohrmüller2023-12-042023-12-042023978-3-8396-1968-1https://doi.org/10.24406/publica-1910https://publica.fraunhofer.de/handle/publica/45101810.24406/publica-1910Fiber reinforced polymers are a composite material used in lightweight construction to reduce weight. The material investigated is a glass fiber reinforced sheet molding compound (SMC), consisting of glass fibers arranged in bundles and a thermoset matrix out of unsaturated polyester polyurethane hybrid resin. This thesis focuses on the characterization of the fiber-matrix interface under mode II (shear) loading and mode I (crack-opening) loading. Therefore, an approach with experiments on the composite material followed by finite element simulations at the microstructural level is chosen. The interface is modeled by a cohesive zone formulation. The interface characterization under mode II loading is done by single-fiber push-out tests. In push-out simulations with thermally induced residual stresses, the effects of neighboring fibers and the influence of the interface normal direction on the test are investigated. In addition, the process of the push-out test is studied in detail in simulations. As a possible interface characterization under mode I loading, the splitting of micropillars with the interface vertically in the middle by a wedge shaped indenter tip is investigated.enfiber reinforced polymersfiber-matrix interfacemechanical characterizationsingle-fiber push-out testmicropillar splitting testDDC::600 Technik, Medizin, angewandte Wissenschaften::620 Ingenieurwissenschaften::621 Angewandte Physikdoctoral thesis