Einfluß sintertechnischer Grenzen für die Herstellung von schwingbeanspruchten Bauteilen aus Sinterstahl

Influence of technical limitations in the production of fatigue loaded PM'Components
 
: Sonsino, C.M.
: Fraunhofer-Institut für Betriebsfestigkeit -LBF-, Darmstadt

Darmstadt: Fraunhofer LBF, 1989, 200 S. : Abb.,Tab.,Lit.
LBF-Bericht, FB-184
Deutsch
Bericht
Fraunhofer LBF ()
Bruchmechanik; constant amplitude loading; fracture mechanic; Kerbwirkung; Lebensdauerlinie; mean stress; Mittelspannung; notch effect; sintered steel; Sinterstahl; Spannungs-Dehnungs-Kurve; stress-strain-curve; variable amplitude loading; Wöhlerlinie; Fertigung; Bauteil; Legierung; Lebensdauer; Sintern; Festigkeit

Abstract
In order to extend the already available knowledge on monotonic and cyclic stressstrain behaviour, fracture mechanical and fatigue properties of mostly used sintered alloys Fe-1.5%Cu, Fe-1.5%Cu-0.6%C, Fe2.0%Cu-2.5%Ni and Fe-0.45%P (delta = 6.6 to 7.3 g/ccm) and to determine the influence of technical limitations in the production of fatigue loaded PM'components, this investigation puts emphasis on following topics: - Influence of sintering time, temperature and atmosphere on the behaviour of the alloys Fe-4.0%Ni-1.5%Cu-0.5%Mo-0.6%C and Fe-2.0%Cu-2.5%Ni (delta = 7.1 g/ccm). - Properties of the alloys Fe-2.0%Ni-0.5%Mo-0.4%C, Fe-1.5%Cu-0.6%C and Fe-2.0%Cu-2.5%Ni after powder forging (delta bigger than 7.7 g/ccm). - Behaviour of the alloy Fe-1.5%Cu (delta = 6.8 and 7.1 g/ccm) manufactured from different iron powders RZ 150, NC 100.24, WPL 150 and WPL 150 smaller than 60 mym. - Influence of different batches of the alloy Fe-1.5%Cu (delta = 6.8, 7.1 and 7.4 g/ccm) and their behaviour after e xposure to salt spray in corrosion protected state and influence of different batches of the alloy Fe-0.45%P (delta = 7.1 and 7.4 g/ccm). - Behaviour of the as sintered and quenched and tempered alloy Fe-0.8%Mn0.95%Cr-0.24%Mo-0.6%C (delta = 7.1 g/ccm). - Variable amplitude of the alloys Fe-4.0%Ni-1.5%Cu-0.5%Mo-0.6%C, Fe2.0%Cu-2.5%Ni (delta = 7.1 g/ccm) and of the above mentioned three powder forged alloys.