Preparation of amorphous FeTa-powders by mechanical alloying

Herstellung amorpher FeTa-Pulver durch mechanisches Legieren
 
: Veltl, G.; Scholz, B.; Kunze, H.-D.

American Powder Metallurgy Institute, Princeton/N.J.; Metal Powder Industries Federation -MPIF-, Princeton/N.J.:
Modern Developments in Powder Metallurgy. Vol.18-21
Princeton/N.J., 1988
S.707-712
Modern Developments in Powder Metallurgy <1988, Orlando/Fla.>
Englisch
Konferenzbeitrag
Fraunhofer IFAM ()
amorphous material; ferrous alloy; glass transition temperature; mechanical alloying; powder technology; tantalum base alloy

Abstract
Amorphous Fe-Ta powders were produced by mechanical alloying. The preparation of the mechanically alloyed FexTa1-x powders was carried out in the composition range 0.2 equal or smaller than = x equal or smaller than = 0.8. The degree of amorphization was monitored by X-ray diffraction measurements. The alloys provide materials with very high crystallization temperatures, up to 1034 deg C at the composition Fe30Ta70.