Materials and device properties of pseudomorphic InxGa1-xAs/Al0.3Ga0.7As/GaAs high electron mobility transistors -0 smaller than x smaller than 0.5.

Material- und Baueigenschaften von pseudomorphen InxGa1-xAs/Al0.3Ga0.7As/GaAs HEMT Strukturen -0 kleiner x kleiner 0.5
 

Applied physics. A 53 (1991), S.109-113 : Abb.,Lit.
ISSN: 0340-3793
ISSN: 0721-7250
ISSN: 0947-8396
Englisch
Zeitschriftenaufsatz
Fraunhofer IAF ()
heterostructure; Heterostruktur; III-V Bauelementeigenschaft; III-V device properties; III-V material properties; III-V Materialeigenschaft

Abstract
Modulation doped Al sub 0.3 As/In sub x GA sub 1-x AS/GaAs high electron mobility transistor structures for device application have been grown using molecular beam epitaxy. Initially the critical layer thickness for InAs mole fractions up to 0.5 was investigated. For InAs mole fractions up to 0.35 good agreement with theoretical considerations was observed. For higher InAs mole fractions disagreement occurred due to a strong decrease of the critical layer thickness. The carrier concentration for Al sub 0.3 Ga sub 0.7 As/In sub x Ga sub 1-x As/GaAs high electron mobility transistor structures with a constant In sub x Ga sub 1-x As quantum well width was investigated as a function of InAs mole fraction. If the In sub x Ga sub1-x As quantum well width is grown at the critical layer thickness the maximum carrier concentration is obtained for an InAs mole fraction of 0.37. A considerable higher carrier concentration in comparison to single-sided delta-doped structures was obtained for the s tructures with delta-doping on both sides of the In sub x Ga sub 1-x As quantum well. Al sub 0.3 Ga 0.7 As/In sub x Ga sub 1-x As/GaAs high electron mobility transistor structures with InAs mole fractions in the range 0-0.35 were fabricated for device application. For the presented field effect transistors best device performance was obtained for InAs mole fractions in the range 0.25-0.3. For the field effect transistors with an InAs mole fraction of 0.25 and a gate length of 0.15 mym a f sub Tau of 115 GHz was measured.