Characterisation of silver thick-film contact formation on textured monocrystalline silicon solar cells

 
: Kontermann, S.; Emanuel, G.; Benick, J.; Preu, R.; Willeke, G.

:
Volltext urn:nbn:de:0011-n-666068 (476 KByte PDF)
MD5 Fingerprint: 43a530f7e97bdabd698da150568712c6
Erstellt am: 29.9.2012


Poortmans, J. ; European Commission, Joint Research Centre -JRC-:
21st European Photovoltaic Solar Energy Conference 2006. Proceedings. CD-ROM : Proceedings of the international conference held in Dresden, Germany, 4 - 8 September 2006
München: WIP-Renewable Energies, 2006
ISBN: 3-936338-20-5
S.613-616
European Photovoltaic Solar Energy Conference <21, 2006, Dresden>
Englisch
Konferenzbeitrag, Elektronische Publikation
Fraunhofer ISE ()

Abstract
The investigations presented in this paper help to clarify the firing temperature dependence of the microstructure at the interface of Ag thick-film contacts on textured silicon solar cells. Textured silicon wafers were chosen to put the investigations in a more relevant environment of a real solar cell. Scanning Electron Microscope (SEM) pictures were taken from silicon wafer surfaces beneath the contact where we found bright and dark regions. We identified them as the SiN layer deposited as an antireflection coating before printing and pure silicon originating from the raw wafer where the SiN layer was completely etched by the glass frit. The percentage of the surface area of the dark regions was quantified and brought into relation with the measured electrical properties and the recorded specific contact resistance. A clear correlation could be shown. The results are discussed referring to models of charge carrier transport in thick-film contacts.