Contact-driven delamination and spalling of coatings due to cyclic shock heating

 
: Semenov, A.S.; Bahr, H.-A.; Balke, H.; Weiß, H.-J.

:

Thin solid films 471 (2005), Nr.1-2, S.200-208
ISSN: 0040-6090
Englisch
Zeitschriftenaufsatz
Fraunhofer IWS ()

Abstract
A new debonding mechanism taking into account crack face contact caused by a thermal gradient during laser heating is considered. The contact renders double influence on the energy release rate G: it leads to sharp increase of G at convergence of two cracks and decreases steady-state value of G. The first feature can explain the laser-induced spalling of thermal barrier coating under combined action of sintering and heating. The inhomogeneous temperature through coating thickness under laser heating can induce contact-driven debonding leading to the spalling under convergence of two cracks. The loading conditions of contact occurrence are derived. The simplified models of contact-driven debonding are proposed and compared with finite element solution.

: http://publica.fraunhofer.de/dokumente/N-57076.html