Recycled Poly(Ethylene Terephthalate)/Clay Nanocomposites

Rheology, Thermal and Mechanical Properties
 
: Chowreddy, R.R.; Nord-Varhaug, K.; Rapp, F.

:

Journal of polymers and the environment 27 (2019), Nr.1, S.37-49
ISSN: 1566-2543
ISSN: 1572-8900
Englisch
Zeitschriftenaufsatz
Fraunhofer ICT ()

Abstract
Polymer nanocomposites containing recycled poly(ethylene terephthalate) (r-PET) as a polymer matrix and Cloisite® 10A as a reinforcement were prepared through melt compounding. First, a masterbatch containing 20 wt% of Cloisite® 10A clay was prepared and later diluted with neat r-PET to obtain nanocomposites containing 1, 2, 4 and 6 wt% of clay. The rheological, thermal, mechanical and morphological properties of the PET–clay nanocomposites were characterized. The complex viscosity of the nanocomposites gradually increases with increase in clay content. The storage modulus and loss modulus of nanocomposite containing 1 wt% of clay was similar to neat r-PET but increases with increase in clay content. Incorporation of clay into a r-PET slightly increases the crystallisation temperature and degree of crystallinity due to the heterogenous nucleating effect of clay. Thermal stability and glass transition temperature of nanocomposite containing Cloisite® 10A clay at lower loadings was similar to r-PET and gradually decreases with increase in clay content. The tensile properties of PET–clay nanocomposites increased gradually with clay content. The impact strength of nanocomposites was not altered until 4 wt% and decreased at 6 wt%. Morphological investigations indicated homogeneous dispersion of clay in r-PET.

: http://publica.fraunhofer.de/dokumente/N-549511.html