In-situ X-ray microscopy of crack-propagation to study fracture mechanics of on-chip interconnect structures

 
: Kutukova, Kristina; Liao, Zhongquan; Werner, Stephan; Guttmann, Peter; Standke, Yvonne; Gluch, Jürgen; Schneider, Gerd; Zschech, Ehrenfried

:

MRS advances 3 (2018), Nr.39, S.2305-2310
ISSN: 2059-8521
Englisch
Zeitschriftenaufsatz
Fraunhofer IKTS ()
adhesive; fracture; in-situ; microelectronic; nanoscale zero-valent iron (nZVI)

Abstract
Chip-package interaction (CPI) and the related thermomechanical stress in microchips increase the risk of failure in on-chip interconnect stacks, caused by delamination along Cu/dielectrics interfaces (adhesive failure) and fracture in dielectrics (cohesive failure). High-resolution transmission X-ray microscopy (TXM) is a unique technique to image crack propagation in on-chip interconnect stacks. The visualization of crack evolution in Cu/low-k Backend-of-Line (BEoL) structures is demonstrated using an experimental setup which combines high-resolution X-ray imaging with mechanical loading. The application of an indenter manipulator at the TXM beamline of the synchrotron radiation source BESSY II provides an unprecedented level of details on the fracture behavior of microchips. This in-situ experiment allows to identify the weakest layers and interfaces and to evaluate the robustness of the BEoL stack against CPI.