Vacuum induced dehydration of swollen poly(methoxy diethylene glycol acrylate) and polystyrene-block-poly(methoxy diethylene glycol acrylate)-block-polystyrene films probed by in-situ neutron reflectivity

 
: Zhong, Qi; Metwalli, Ezzeldin; Rawolle, Monika; Kaune, Gunar; Bivigou-Koumba, Achille M.; Laschewsky, André; Papadakis, Christine M.; Cubitt, Robert; Wang, Jiping; Müller-Buschbaum, Peter

:

Polymer 124 (2017), S.263-273
ISSN: 0032-3861
Deutsche Forschungsgemeinschaft DFG
SPP 1259; La611/7
Struktur und Kinetik stimuli-responsiver, dünner Hydrogelfilme aus amphiphilen Blockcopolymeren
Englisch
Zeitschriftenaufsatz
Fraunhofer IAP ()
block copolymer; hydrogel; polymer coating; phase transition; LCST; dehydration; n-situ neutron reflectivity

Abstract
The isothermal vacuum-induced dehydration of thin films made of poly(methoxy diethylene glycol acrylate) (PMDEGA), which were swollen under ambient conditions, is studied. The dehydration behavior of the homopolymer film as well as of a nanostructured film of the amphiphilic triblock copolymer polystyrene-block-poly(methoxy diethylene glycol acrylate)-block-polystyrene, abbreviated as PS-b-PMDEGA-b-PS, are probed, and compared to the thermally induced dehydration behavior of such thin thermo-responsive films when they pass through their LCST-type coil-to globule collapse transition. The dehydration kinetics is followed by in-situ neutron reflectivity measurements. Contrast results from the use of deuterated water. Water content and film thickness are significantly reduced during the proce ss, which can be explained by Schott second order kinetics theory for both films. The water content of the dehydrated equilibrium state from this model is very close to the residual water content obtained from the final static measurements, indicating that residual water still remains in the film even after prolonged exposure to the vacuum. In the PS-b-PMDEGA-b-PS film that shows micro-phase separation, the hydrophobic PS domains modify the dehydration process by hindering the water removal, and thus retarding dehydration by about 30%. Whereas residual water remains tightly bound in the PMDEGA domains, water is completely removed from the PS domains of the block copolymer film.