Radiation-induced loss of optical fibres at 1300 nm and 1550 nm wavelength

 
: Henschel, H.; Köhn, O.; Schmidt, H.U.

:
Postprint urn:nbn:de:0011-n-2712 (167 KByte PDF)
MD5 Fingerprint: a48a475e3bc014b1a6b72a126971ad89
Copyright 1996 Society of Photo-Optical Instrumentation Engineers. One print or electronic copy may be made for personal use only. Systematic reproduction and distribution, duplication of any material in this paper for a fee or for commercial purposes, or modification of the content of the paper are prohibited.
Erstellt am: 25.9.2010


Taylor, E.W. ; Society of Photo-Optical Instrumentation Engineers -SPIE-, Bellingham/Wash.:
Photonics for space environments IV : 6-7 August 1996, Denver, Colorado
Bellingham/Wash.: SPIE, 1996 (SPIE Proceedings Series 2811)
ISBN: 0-8194-2199-5
S.68-76
Conference on Photonics for Space Environments <4, 1996, Denver/Colo.>
Englisch
Konferenzbeitrag, Elektronische Publikation
Fraunhofer INT ()
1300 nm; 1550 nm; annealing time; irradiation time; gamma irradiation; irradiation time variation; optical fibres; radiation induced loss

Abstract
The radiation-induced loss of single mode fibres with undoped and Ge-doped core material was measured at 1300 nm and 1550 nm in the time range from 0.1 s to < 500000 s at room temperature (+25øC). With the Ge-doped fibre, measurements were also made at -50øC and +80øC. The ratio of the losses at 1300 nm and 1550 nm increased at +25øC with both fibre types within about 10 s to a maximum value of ÷2 (Ge-doped) or ÷ 2.7 (undoped). Then the ratio decreased continuously and became < 1 (= higher loss at 1550 nm) after about 35000 - 70000 s (Ge-doped) or > 350000 s (undoped). After ÷ 500000 s a value of ÷ 0.75 was reached with the Ge-doped fibre, with an observable tendency to fall further. At -50øC the ratio increased up to about 2.2 and remained constant (as if frozen) during the whole irradiation time of 500000 s. At +80øC, however, the radiation-induced loss at 1550 nm was higher at the beginning and became lower than the one at 1300 nm only after an irradiation time of > 10E+4 s. Additi ally the annealing time of loss was measured after the end of irradiation for varying irradiation times between about 3 s and 400000 s. The results can qualitatively explain the radiation-induced loss curves at 1300 nm and 1550 nm as well as their ratio.on