Identification of As-vacancy complexes in Zn-diffused GaAs

 
: Elsayed, M.; Krause-Rehberg, R.; Korff, B.; Richter, S.; Leipner, H.S.

:

Journal of applied physics 113 (2013), Nr.9, Art.094902, 9 S.
ISSN: 0021-8979
ISSN: 1089-7550
Englisch
Zeitschriftenaufsatz
Fraunhofer CSP ()

Abstract
We have used positron annihilation spectroscopy to study the introduction of point defects in Zn-diffused semi-insulating GaAs. The diffusion was performed by annealing the samples for 2 h at 950 degrees C. The samples were etched in steps of 7 mu m. Both Doppler broadening using slow positron beam and lifetime spectroscopy studies were performed after each etching step. Both techniques showed the existence of vacancy-type defects in a layer of about 45 mu m. Secondary ion mass spectroscopy measurements illustrated the presence of Zn at high level in the sample almost up to the same depth. Vacancy-like defects as well as shallow positron traps were observed by lifetime measurements. We distinguish two kinds of defects: As vacancy belongs to defect complex, bound to most likely one Zn atom incorporated on Ga sublattice, and negative-ion-type positron traps. Zn acceptors explained the observation of shallow traps. The effect of Zn was evidenced by probing GaAs samples annealed under similar conditions but without Zn treatment. A defect-free bulk lifetime value is detected in this sample. Moreover, our positron annihilation spectroscopy measurements demonstrate that Zn diffusion in GaAs system is governed by kick-out mechanism.

: http://publica.fraunhofer.de/dokumente/N-241878.html