Optimization of the property profile of poly-L-lactide by synthesis of PLLA-polystyrene - block copolymers

 
: Dorff, G.; Hahn, M.; Laschewsky, A.; Lieske, A.

:

Journal of applied polymer science 127 (2013), Nr.1, S.120-126
ISSN: 0021-8995
ISSN: 1097-4628
Englisch
Zeitschriftenaufsatz
Fraunhofer IAP ()

Abstract
Diblock and triblock copolymers of poly-L-lactide (PLLA) and polystyrene (PS) were synthesized and the mechanical properties of these copolymers studied. Free radical polymerization of styrene in the presence of 2-mercaptoethanol as functional chain transfer agent produced mono-functionalized PS-blocks which were used as macroinitiators in the subsequent ring opening polymerization (ROP) of L-lactide to produce the diblock copolymers. Furthermore a --bishydroxyl functionalized PS-block was synthesized by RAFT, which was then engaged as bifunctional initiator for the ROP of L-lactide to provide the triblock copolymers PLLA-PS-PLLA. Through the copolymerisation and high molar masses, it was possible to achieve an improved mechanical property profile, compared with pure PLLA, or the analogous blends of PLLA and PS. A weight fraction of PS of 10-30% was found to be the optimal range for improving the heat deflection temperature (HDT), as well as mechanical properties such a s ultimate tensile strength or elongation at break.

: http://publica.fraunhofer.de/dokumente/N-206565.html