Wet etching studies of silicon nitride thin films deposited by electron cyclotron resonance (ECR) plasma enhanced chemical vapor deposition

Nasschemisches Ätzen von Siliziumnitrid Dünnfilm hergestellt mittels ECR-PECVD Technik
 
: Sundaram, K.B.; Sah, R.E.; Baumann, H.; Balachandran, K.; Todi, R.M.

:

Microelectronic engineering 70 (2003), Nr.1, S.109-114
ISSN: 0167-9317
Englisch
Zeitschriftenaufsatz
Fraunhofer IAF ()
silicon nitride film; Siliziumnitrid Dünnfilm; dielectric film; dielektrische Schichten; plasma deposition; Plasma Abscheidung; RBS study; RBS-Untersuchung

Abstract
Silicon nitride films of various compositions have been deposited on silicon substrate by electron cyclotron resonance plasma-enhanced chemical vapor deposition (ECR-PECVD) technique from mixtures of Ar, N2 and SiH4 as precursors. Film composition and refractive index as a function of deposition parameters like gas flow ratio and pressure were studied. Wet etching studies were conducted using diluted phosphoric acid and buffered oxide etch (BOE) solutions of various concentrations. The etching studies using phosphoric acid were conducted in the temperature range of 70-90 °C. For BOE the temperature range was 25-55 °C. The etch rate with BOE solution is much higher than with phosphoric acid. The results indicate that the mechanism of etching with phosphoric acid is different from that with BOE solution.