Nondestructive characterization of neutron induced embrittlement in nuclear pressure vessel steel microstructure by using electromagnetic testing

: Altpeter, Iris; Dobmann, Gerd; Hübschen, Gerhard; Kopp, Melanie; Tschuncky, Ralf

Volltext urn:nbn:de:0011-n-1781034 (850 KByte PDF)
MD5 Fingerprint: f50aba31b5091ac4954e4796e1845330
Erstellt am: 25.8.2011

Deutsche Gesellschaft für Zerstörungsfreie Prüfung e.V. -DGZfP-, Berlin:
8th International Conference on NDE in Relation to Structural Integrity for Nuclear and Pressurised Components 2010. CD-ROM : Berlin, Germany, from 29th of September to 1st of October 2010
Berlin, 2011 (DGZfP Proceedings BB 125)
Paper Fr.2.C.5, 7 S.
International Conference on NDE in Relation to Structural Integrity for Nuclear and Pressurised Components <8, 2010, Berlin>
Konferenzbeitrag, Elektronische Publikation
Fraunhofer IZFP ()

By using nuclear power for energy generation the pressure vessel wall is exposed to neutron fluences of different levels depending on the distance to the core. Hence materials undergo a change in their microstructure in terms of embrittlement, to be measured as toughness reduction and shift of the Ductile-to-Brittle Transition Temperature (DBTT) to higher temperatures. Normally plant safety concerning this change in microstructure is assured by destructively testing surveillance samples. These are standard tensile and ISO V-specimen which consist of exactly the same material as the pressure vessel and its weld metal, being exposed to accelerated irradiation rates within special irradiation channels allowing a pronounced ageing. It is demonstrated that electromagnetic parameters allow to characterize the changes in the microstructure generated through neutron irradiation. After a defined calibration process a quantitative characterization of the embrittlement especially in terms of the shift of the DBTT is possible. This has been demonstrated for reactor pressure vessel steels used in nuclear power plants of eastern and western designs. As testing methods 3MA (Micromagnetic, Multiparameter, Microstructure and stress Analysis) [1] and the dynamic magnetostriction using EMAT (Electromagnetic Acoustic Transducers) have been applied in a nondestructive combination measurement system.
Further experiments show the possibility to measure 3MA and dynamic magnetostriction quantities through an 8 mm thick austenitic stainless steel cladding.