Resonant Raman scattering from buried Al(x)Ga(1-x)N (x < = 0.17) layers in (Al,Ga,In)N heterostructures

Resonante Ramanstreuung an vergrabenen Al(x)Ga(1-x)N (x < = 0.17) Schichten in (Al,Ga,In)N Heterostrukturen
 
: Yoshikawa, M.; Wagner, J.; Obloh, H.; Kunzer, M.; Maier, M.

:

Journal of applied physics 87 (2000), Nr.6, S.2853-2856
ISSN: 0021-8979
ISSN: 1089-7550
Englisch
Zeitschriftenaufsatz
Fraunhofer IAF ()
AlGaN; heterostructures; Hetersostrukturen; raman spectroscopy; Ramanspektroskopie; resonant Raman scattering; resonante Ramanstreuung

Abstract
Resonant Raman scattering from Al(x)Ga(1-x)N(x<=0,17)) layers in (Al, Ga,In)N heterostructures has been studied using optical excitation at a photon energy of h v (L) =3.72 eV (333.61 nm). Tuning of the AlGaN band-gap energy, and thus of the resonance condition, was achieved by variation of the sample temperature. A pronounced outgoing resonance behavior was observed for first- and second-order Raman scattering by the AlGaNA(l) (LO) phonon, which allows a separation of the AlGaN LO phonon signal from the corresponding GaN phonon line even in the presence of much thicker surrounding GaN layers. The composition dependence of the Al(x)Ga(1-x)NA(l) (LO) phonon mode was determined to omega(LO)(x)=734+356.8x-814.7x(exp 2) cm (exp -1) for the present excitation conditions (h v l=3.72eV) and composition range (x<=0.17). The use of resonantly enhanced Raman scattering by the AlGaN A(l)(LO) phonon allowed us to assess nondestructively the composition of the AlGaN cladding layers in an (Al, Ga, In)N laser structure, even though the Raman spectrum recorded for nonresonant subband-gap excitation was completely dominated by scattering from the much thicker GaN layers in the structure.