Influence of the oxidation temperature and atmosphere on the reliability of thick gate oxides on the 4H-SiC C(000-1) face

 
: Grieb, M.; Peters, D.; Bauer, A.J.; Friedrichs, P.; Ryssel, H.

:

Suzuki, A.:
Silicon carbide and related materials 2007. Pt.2 : Selected, peer reviewed papers from the International Conference on Silicon Carbide and Related Materials 2007, Otsu Prince Hotel Convention Hall, Lake Biwa Resort, Otsu, Japan, October 14 - 19, 2007
Stafa-Zürich: Trans Tech Publications, 2009 (Materials Science Forum 600/603)
ISSN: 0255-5476
pp.597-602
International Conference on Silicon Carbide and Related Materials (ICSCRM) <12, 2007, Otsu>
English
Conference Paper
Fraunhofer IISB ()

Abstract
The reliability of thermal oxides grown on n-type 4H-SiC C(000-1) face wafer has been investigated. In order to examine the influence of different oxidation atmospheres and temperatures on the reliability, metal-oxide-semi conductor capacitors were manufactured and the different oxides were characterized by C-V measurements and constant-current-stress. The N2O-oxides show the smallest flat band voltage shift compared to the ideal C-V curve and so the lowest number of effective oxide charges. They reveal also the lowest density of interface states in comparison to the other oxides grown on the C(000-1) face, but it is still higher than the best oxides on the Si(000-1) face. Higher oxidation temperatures result in smaller flat band voltage shifts and lower interface state densities. Time to breakdown measurements show that the charge-to-breakdown value of 63% cumulative failure for the N2O-oxide on the C(000-1) face is more than one order of magnitude higher than the highest values measured on the Si(000-1) face. Therefore it can be concluded that a smaller density of interface states results in a higher reliability of the oxide.