MOCVD of tantalum nitride thin films from TBTEMT single source precursor as metal electrodes in CMOS applications

 
: Lemberger, M.; Thiemann, S.; Baunemann, A.; Parala, H.; Fischer, R.A.; Hinz, J.; Bauer, A.J.; Ryssel, H.

:

Matthews, A.:
Proceedings of the 16th European Conference in Chemical Vapor Deposition, EUROCVD-16 : The Hague, the Netherlands, September 16 - 21, 2007
Amsterdam: Elsevier, 2007 (Surface and coatings technology 201.2007, Nr.22/23)
pp.9154-9158
European Conference in Chemical Vapor Deposition (EUROCVD) <16, 2007, The Hague>
English
Conference Paper, Journal Article
Fraunhofer IISB ()

Abstract
Tantalum nitride films obtained by MOCVD using a tert-butylimido-tris-ethylmethylamido-tantalum (TBTEMT, Ta(NCMe3)(NEtMe)(3)) compound were physically and electrically investigated. Lowest resistivity of 2.5 m Omega cm was obtained at 600 degrees C and 0.25 mbar total pressure. Deposition rate under these conditions was 4 nm/min, but step coverage was poor. Values of 50 to 75% are obtained at the side walls (10% of trench depth) and 25% at the bottom of a 5 gin deep trench with an aspect ratio of 2:1. Film analysis by XPS reveals Ta rich layers (e.g., Ta:N ratios of 1:0.85 for 400 degrees C and 1:0.6 for 650 degrees C deposition temperature, respectively) with a high oxygen contents of about 35 at.%. Oxygen contamination is due to both, continuous incorporation during film growth caused by leakage of the reactor and post-deposition oxidation. TaN electrodes deposited at 600 degrees C and 0.25 mbar reveal a metal work function of about 4.5 eV independent on thickness of TaN. However, thicker TaN layers show lower leakage current densities. Post-deposition annealing at 900 degrees C for 10 s does not cause changes in TaN layer thickness, resistivity, or oxide charge, though annealing in NH3 atmosphere reduces 0 contamination. Leakage current densities of annealed MOS capacitors (900 degrees C, 10 s, NH3) are reduced by nearly one order of magnitude, but leakage current characteristics are strongly degraded after post-deposition annealing. Metal work function is shifted towards mid gap and, in dependence on TaN layer thickness, values of 4.65 eV (90 nm TAN) to 4.79 eV (30 nm TaN) are obtained.