Probing traps in the persistent phosphor SrAl2O4:Eu2+, Dy3+,B3+ - a wavelength, temperature and sample dependent thermoluminescence investigation

: Bierwagen, Jakob; Delgado, Teresa; Jiranek, Guillaume; Yoon, Songhak; Gartmann, Nando; Walfort, Bernhard; Pollnau, Markus; Hagemann, Hans


Journal of luminescence 222 (2020), Art. 117113
ISSN: 0022-2313
Journal Article
Fraunhofer IWKS ()

Wavelength-dependent thermoluminescence (TL) experiments were performed on SrAl2O4:Eu, SrAl2O4:Eu,B, SrAl2O4:Eu,Dy and SrAl2O4:Eu,Dy,B polycrystalline samples. Excitation at 445 nm allows to selectively excite one of the two different Eu2+ ions substituting for Sr in the crystal, whereas excitation at 375 nm excites both Eu2+ ions. Incorporation of boron generates the deepest traps which contribute to the very long afterglow in this material, while dysprosium increases significantly (by a factor of about 4–8) the total number of traps involved in the afterglow of this persistent phosphor. Increasing the temperature at which the samples are irradiated (loaded) from 173 K to 248 K reveals that many new traps can only be occupied or activated at higher temperatures, leading to a strong increase of the integrated TL intensity, in particular for the Dy-containing samples. Boron does not appear to contribute to these thermally-activated traps significantly responsible for the long afterglow of SrAl2O4:Eu,Dy,B. The results of this study reveal that the diversity of traps leading to the long afterglow is much larger than previously reported in the literature. We propose that boron stabilizes F centers (which absorb in the far UV), while the presence of dysprosium induces an excitation-induced charge-transfer reaction Eu2+ + Dy3+ → Eu3+ + Dy2+. However, the principal traps responsible for the efficient afterglow are temperature-activated and appear to be associated with the green emitting Eu2+ ion on the Sr2 site coupled to a nearby dysprosium ion.