Contacting Methods for C12A7 Electride Ceramic

 
: Wätzig, Katja; Rost, Axel; Schilm, Jochen; Tajmar, M.; Michaelis, Alexander

:

Journal of Ceramic Science and Technology (2020), No.1, pp.11-16
ISSN: 2190-9385
European Commission EC
H2020; 828902; E.T.PACK
Electrodynamic Tether Technology for Passive Consumable-less Deorbit Kit
English
Journal Article
Fraunhofer IKTS ()
electron emitter; conductive ceramic; C12A7; calcium aluminate; contacting metallization

Abstract
C12A7:e- ([Ca24Al28O64]4+4e-) ceramic is a material with high electrical conductivity and low work function, so that this ceramic is suitable as an electron-emitting material. Although the bulk material indicates these extraordinary properties, the surface of the ceramic is insulating. Therefore, a metallization film is needed to realize an electrical contact with low ohmic losses for the application of the material. In this study, we investigated three different metal pastes (Pt, Au and Cusil-ABA®) for contacting the surface and measured the reduction of the resistance during the firing process of the pastes. The resistance of the contacted C12A7:e- was determined as a function of the temperature under nitrogen atmosphere. Additionally, the oxidation behaviour of the electride was observed based on increasing resistance when the material was heated in air. The lowest resistance was measured with Ag-based braze (Cusil-ABA®), however, cracking of the contacted ceramic was observed. Alternatively, contacting with Au reached a specific resistance of 5.4 Ω cm (T = 800 °C).