Extrusion Coating of Paper with Poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV) - Packaging Related Functional Properties

: Sängerlaub, Sven; Brüggemann, Marleen; Rodler, Norbert; Jost, Verena; Bauer, Klaus Dieter

Fulltext ()

Coatings 9 (2019), No.7, Art. 457, 28 pp.
ISSN: 2079-6412
Journal Article, Electronic Publication
Fraunhofer IVV ()

Taking into account the current trend for environmentally friendly solutions, paper coated with a biopolymer presents an interesting field for future packaging applications. This study covers the application of the biopolymer poly(3-hydroxybutyrate-co-3-hydroxyvalerate) (PHBV) on a paper substrate via extrusion coating. The intention of this study is to analyse the effect of a plasticiser on the processability (melting point, film thickness) and the final properties (crystallinity, elongation at break) of PHBV. Up to 15 wt.% of the plasticisers triethyl citrate (TEC) and polyethylene glycol (PEG) were used as additive. The processing (including melt flow rate) as well as the structural properties (melting and crystallisation temperature, surface structure by atomic force microscopy (AFM), polarisation microscopy, scanning electron microscopy (SEM)), mechanical properties (elongation at break, tensile strength, elastic modulus, adhesion), and barrier properties (grease) of these blends and their coating behaviour (thickness on paper), were tested at different extrusion temperatures. The melting temperature (Tm) of PHBV was reduced by the plasticisers (from 172 °C to 164 resp. 169 °C with 15 wt.% TEC resp. PEG). The minimal achieved PHBV film thickness on paper was 30 µm owing to its low melt strength. The elastic modulus decreased with both plasticisers (from 3000 N/mm2 to 1200 resp. 1600 N/mm2 with 15 wt.% TEC resp. PEG). At 15 wt.% TEC, the elongation at break increased to 2.4 length-% (pure PHBV films had 0.9 length-%). The grease barrier (staining) was low owing to cracks in the PHBV layers. The extrusion temperature correlated with the grease barrier, mechanical properties, and bond strength. The bond strength was higher for films extruded with a temperature profile for constant melt flow rate at different plasticiser concentrations. The bond strength was max. 1.2 N/15 mm. Grease staining occurs because of cracks induced by the low elongation at break and high brittleness. Extrusion coating of the used specific PHBV on paper is possible. In further studies, the minimum possible PHBV film thickness needs to be reduced to be cost-effective. The flexibility needs to be increased to avoid cracks, which cause migration and staining.