Elemental evolution of the SiOxFy self-masking layer of plasma textured silicon and its modification during air exposure

 
: Gaudig, M.; Hirsch, J.; Naumann, V.; Werner, M.; Grosser, S.; Hagendorf, C.; Bernhard, N.; Lausch, D.

:

Journal of applied physics 121 (2017), No.6, Art. 063301, 9 pp.
ISSN: 0021-8979
ISSN: 1089-7550
Bundesministerium für Bildung und Forschung BMBF
03SF0417A
English
Journal Article
Fraunhofer CSP ()

Abstract
The influence of the SiOxFy selfmasking process on the formation of black-Silicon (b-Si) textures by maskless SF6/O-2 plasma etching is of great interest with regard to the optimization of the texturing process for highly antireflective silicon. For that reason, the elemental composition of plasma textured silicon surfaces is analyzed by transmission electron microscopy and X-ray photoelectron spectroscopy. The chemical composition of a fluorine containing oxide layer on top of the surface was confirmed and determined quantitatively. A strongly reduced F content was found after ambient air exposure. A qualitative model of the chemical and physical processes caused by maskless plasma texturing was developed to explain the observed experimental results. The decrease in the F content is assumed to be caused by hydrolysis of F by air moisture, resulting in a successive desorption of HF and transformation of SiOxFy to silicon oxide.