Influence of the applied power on the barrier performance of silicon-containing plasma polymer coatings using a hollow cathode-activated PECVD process

: Top, Michiel; Fahlteich, John; Hosson, Jeff T.M. de


Plasma Processes and Polymers 14 (2017), No.9, Art. 1700016, 8 pp.
ISSN: 1612-8850
ISSN: 1612-8869
Journal Article
Fraunhofer FEP ()
barrier; DC discharge; hexamethyldisiloxane; HMDSO; hollow cathode; plasma polymerization

A hollow cathode arc discharge is used for the roll-to-roll deposition of silicon-containing plasma polymer thin films on a polymer substrate. It is found that the fragmentation of the used monomer hexamethyldisiloxane (HMDSO) increases with increasing plasma power. The higher fragmentation was related to a reduced hydrogen content as a result of breaking C[BOND]H bonds. This allowed for a higher degree of cross-linking. The latter has a positive effect on the barrier performance of the coatings. A hollow cathode arc discharge with separate anode allowed the deposition of a plasma polymer with a water vapor transmission rate (WVTR) of 0.16 g m−2 day−1 (measured at 38 °C and 90% r.h.) on a PET substrate while maintaining a deposition rate of approximately 450 nm m min−1.