Seed-mediated hot-injection synthesis of tiny Ag nanocrystals on nanoscale solid supports and reaction mechanism

: Barhoum, A.; Rehan, M.; Rahier, H.; Bechelany, M.; Assche, G. van


ACS applied materials & interfaces 8 (2016), No.16, pp.10551-10561
ISSN: 1944-8244
ISSN: 0013-936X
ISSN: 1944-8252
Journal Article
Fraunhofer IFAM ()

Controlling the size and shape of noble Ag nanocrystals (NCs) is of great interest because of their unique size-and shape-dependent properties, especially below 20 nm, and because of interesting applications in drug delivery, sensing, and catalysis. However, the high surface energy and tendency of these tiny NCs to aggregate deteriorates their unique properties and limits their applications. to avoid the aggregation of Ag NCs and improve their performance, we report a. seed-mediated hot injection approach to synthesize highly dispersed tiny Ag NCs on a nanosized solid CaCO3 support. This simple, low-cost, and effective chemical approach allows for synthesizing highly uniform Ag NCs (similar to 10 nm) on the surface of presynthesized CaCO3 single NCs (similar to 52 nm) without any aggregation of the Ag NCs. Viscose fibers were coated with the Ag@CaCO3 composite nanoparticles (NPs) produced, as well as with similar to 426 nm Ag NPs for reference. The Ag@CaCO3 composite NPs show excellent UV protection and antibacterial activity against Escherichia coli. In addition, they give a satin sheen gold to a dark gold color to the viscose fibers, while the Ag NPs (similar to 426 nm) result in a silver color. The proposed synthesis approach is highly versatile and applicable for many other noble metals, like Au or Pt.