Large- and small-angle grain boundaries in multi-crystalline silicon and implications for the evolution of grain boundaries during crystal growth

 
: Carl, E.R.; Danilewsky, A.; Meissner, E.; Geiger, T.

:

Journal of Applied Crystallography 47 (2014), pp.1958-1965
ISSN: 0021-8898
English
Journal Article
Fraunhofer IISB ()

Abstract
A detailed study of twin-, large-angle and small-angle grain boundaries over a small volume of multi-crystalline silicon is presented on the basis of electron backscatter diffraction and synchrotron X-ray topography (SXRT) measurements. Identical areas (ca 6 mm 2) of two nearest neighbour wafers from a directional solidified Si column were analysed in order to gain information about the evolution of grain boundaries during the crystal growth process. Therefore, the emphasis was placed on the evolution of one particular grain and its neighbouring grains. In the case of 'straight line' Sigma 3 grain boundaries, no change is observed if the twin plane corresponds to a {211} plane. Significant changes are found for non-straight line boundaries: while curved Sigma 3 grain boundaries are formed and eliminated very frequently, the Sigma 9 and Sigma 27a grain boundaries undergo only minor changes. By means of SXRT imaging, it is shown that the microstructure of the analysed grain exhibits numerous small-angle grain boundaries with angles in the range between 0.003 and 0.02 degrees, corresponding to a theoretical dislocation density of the order of 10(7)-10(8) cm(-2). The experiments give evidence that the small-angle grain boundaries with the larger angles extend, while those with smaller angles vanish during growth.

: http://publica.fraunhofer.de/documents/N-324320.html