Fracture mechanics in new designed power module under thermo-mechanical loads

 
: Durand, C.; Klingler, M.; Coutellier, D.; Naceur, H.; Grams, A.; Wittler, O.

:

Buffière, J.Y. ; Societe Francaise de Metallurgie et de Materiaux -SF2M-, Paris:
Fatigue Design & Material Defects, FDMD II - JIP 2014 : 14th International Spring Meeting - SF2M Commission Fatigue, Paris, June 11-13 2014
Les Ulis: EDP Sciences, 2014 (MATEC Web of Conferences 12.2014)
ISBN: 978-2-7598-1274-5
Art. 04015, 3 pp.
International Symposium on Fatigue Design & Material Defects" (FDMD) <2, 2014, Paris>
Société Française de Métallurgie et de Matériaux (SF2M International Spring Meeting) <14, 2014, Paris>
English
Conference Paper
Fraunhofer IZM ()

Abstract
Thermo-mechanically induced failure is a major reliability issue in the microelectronic industry. On this account, a new type of Assembly Interconnected Technology used to connect MOSFETs in power modules has been developed. The reliability is increased by using a copper clip soldered on the top side of the chip, avoiding the use of aluminium wire bonds, often responsible for the failure of the device. Thus the new designed MOSFET package does not follow the same failure mechanisms as standard modules. Thermal and power cycling tests were performed on these new packages and resulting failures were analyzed. Thermo-mechanical simulations including cracks in the aluminium metallization and intermetallics (IMC) were performed using Finite Element Analysis in order to better understand crack propagation and module behaviour.