Titel
Electromigration early failure void nucleation and growth phenomena in Cu and Cu(Mn) interconnects
Abstract
Electromigration early failure void nucleation and growth phenomena were studied using large-scale, statistical analysis methods. A total of about 496,000 interconnects were tested over a wide current density and temperature range (j = 3.4 to 41.2 µmA/m2, T = 200 to 350°C) to analyze the detailed behavior of the current density exponent n and the activation energy Ea. The results for the critical V1M1 downstream interface indicate a reduction from n = 1.55±0.10 to n = 1.15±0.15 when lowering the temperature towards 200°C for Cu-based interconnects. This suggests that the electromigration downstream early failure mechanism is shifting from a mix of nucleation-controlled (n = 2) and growth-controlled (n = 1) to a fully growth-controlled mode, assisted by the increased thermal stress at lower temperatures (especially at use conditions). For Cu(Mn)-based interconnects, a drop from n = 2.00±0.07 to n = 1.64±0.2 was found, indicating additional effects of a superimposed incuba tion time. Furthermore, at lower current densities, the Ea value seems to drop for both Cu and Cu(Mn) interconnects by a slight, but significant amount of 0.1 - 0.2eV. Implications for extrapolations of accelerated test data to use conditions are discussed. Furthermore, the scaling behavior of the early failure population at the NSD=-3 level (F about 0.1%) was analyzed, spanning 90, 65, 45, 40 and 28 nm technology nodes.