New approach for chromate free coatings in aircraft applications: Modified zinc pigments

 
: Zockoll, A.; Weise, J.; Plagemann, P.

:

Warrendale, Pa.: SAE, 2011
SAE Technical Papers, 2011-01-2741
AeroTech Congress and Exhibition (AEROTECH) <2011,Toulouse>
English
Report
Fraunhofer IFAM ()

Abstract
Alternatives for the environmentally harmful Cr(VI)-based protective coatings for aluminium alloys are highly demanded, especially for aircraft application a. So far, suitable alternative pigments providing inhibiting effects which are comparable to the performance of chromates have not been found. Well known pigments used in corrosion protection coatings are zinc pigments for steel substrates - offering cathodic protection to the substrate and a densification of the coating due to the volume expansion of its corrosion products. Furthermore, it is generally assumed that zinc corrosion products also offer an inhibiting effect. Due to their lower electrochemical potential zinc does not provide cathodic protection to aluminium substrates. To transfer the positive protection effects of zinc to the application of protective coatings on aluminium substrates, zinc pigments have been successfully modified by alloying with magnesium. Mg-Zn-alloys were prepared in different compo sitions with special attention to the intermetallic phases like MgZn, and Mg 2Zn3. Pigments were prepared and included in a coating system. Pickled samples of AA 2024 unclad were coated and the corrosion behaviour investigated. A durability of more than 10 000 hours in salt spray test could already be achieved. Additional measurements showed a significant influence of the pigment micro-structure on the electrochemical behaviour of the intermetallic pigments. Copyright

: http://publica.fraunhofer.de/documents/N-263755.html