Influence of tantalum on the microstructure and properties of Ti(C,N)-Ni cermets

 
: Naidoo, M.; Johnson, O.; Sigalas, I.; Herrmann, M.

:

International journal of refractory metals and hard materials 42 (2014), pp.97-102
ISSN: 0263-4368
English
Journal Article
Fraunhofer IKTS ()
cermets; mechanical alloying; spark plasma sintering; Ta; Ti(C,N)

Abstract
Several (Ti,Ta)(C,N) cermets were prepared from Ti(C,N) and Ta powder with or without Ni. For comparison, Ti(C,N) with Ni were also prepared. The mixed powders were sintered at 1400-1500 °C by FAST/SPS up to a density higher than 99% theoretical density. The addition of Ta delays densification of Ti(C,N)-Ni cermets due to the formation of intermetallic phases. During sintering, the Ta was incorporated into the Ti(C,N), forming solid solution, thus changing the core-rim structure of the Ti(C,N) cermets. On the other hand, the Ta additions result in grain refinement and improved hardness (from 16.1 GPa to 17.8 GPa) and fracture toughness (from 5.5 MPa.m1/2 to 6.9 MPa.m1/2).

: http://publica.fraunhofer.de/documents/N-261228.html