Comparison of thermo-mechanical characteristics of non-doped and 3 mol% B-site Zr-doped Ba0.5Sr0.5Co0.8Fe0.2O3-sigma

 
: Pecanac, G.; Kiesel, L.; Kriegel, R.; Malzbender, J.

:

Ceramics international : CI 40 (2014), No.1, Pt.B, pp.1843-1850
ISSN: 0272-8842
English
Journal Article
Fraunhofer IKTS ()
C. Creep; C. Strength; ceramics; E. Membranes; subcritical crack growth

Abstract
A dense membrane layer supported by a thick porous substrate is a favorable design for advanced oxygen separation units used in Oxy-fuel processes and membrane reactors. Based on the highest permeation rates verified so far, Ba0.5Sr0.5Co0.8Fe0.2O3-sigma appears to be the most promising membrane and substrate material. This material, however, suffers from partial decomposition of cubic structure to hexagonal polymorphs at about 825 °C, which is associated with a significant oxygen permeation drop. The partial substitution of the B-site with 3 mol% zirconium has been suggested as one of solutions for suppressing this transformation. The current study concentrated on the comparison of the thermo-mechanical characteristics of doped and non-doped Ba0.5Sr0.5Co0.8Fe0.2O3-sigma. Although the l ater material showed higher elastic modulus and fracture strength in absolute values, overall their characteristics mostly agree. It was shown that shortening of the membrane tube from 1 m to half its length should not influence fracture strength significantly. Fractographic analysis ruled out the cutting edge effect in O-ring bending.

: http://publica.fraunhofer.de/documents/N-258170.html