Influence and effectivity of VC and Cr3C2 grain growth inhibitors on sintering of binderless tungsten carbide

 
: Poetschke, Johannes; Richter, Volkmar; Holke, Roland

:

International journal of refractory metals and hard materials 31 (2012), pp.218-223
ISSN: 0263-4368
English
Journal Article
Fraunhofer IKTS ()
WC; binderless hardmetal; binderless cemented carbide; SPS; abnormal grain growth; vanadium carbide; chromium carbide

Abstract
For the production of hard, high temperature and abrasion resistant parts, like water-jet nozzles or pressing tools for forming glass lenses, binderless cemented carbide is used. In this work, the consolidation of tungsten carbide with additions of VC and Cr3C2 grain growth inhibitors is studied. Tungsten carbide powder dry or wet milled was consolidated by dry pressing, debindering and gas pressurized sintering and, alternatively, by spark plasma sintering. The effect of adding VC and Cr3C2 to binderless tungsten carbide on the grain growth was studied with contents being 0; 0.1; 0.3; 0.5; 0.7 and 1.0 wt.%. Samples with an ultrafine microstructure free of abnormal grain growth, a hardness of 25.5 GPa and a fracture toughness of 7.2 MPa·m1/2 were archived by conventional sintering. Both ca rbides reduce grain growth, but with Cr3C2 a finer microstructure can be achieved at lower amounts. Compared to the same amount of Cr3C2, the addition of VC results in smaller grains but lower hardness and fracture toughness.