Ultrahigh boron doping of nanocrystalline diamond films and their electron field emission characteristics

 
: Jiang, X.; Au, F.C.K.; Lee, S.-T.

:

Journal of applied physics 92 (2002), No.5, pp.2880-2883
ISSN: 0021-8979
ISSN: 1089-7550
English
Journal Article
Fraunhofer IST ()
boron; diamond; electron field emission; elemental semiconductors; grain size; heavily doped semiconductors

Abstract
Heavily boron-doped nanocrystalline (nc) diamond films were deposited using microwave plasma chemical vapor deposition process in which the growing film surface was continuously bombarded by H/sup +/ and hydrocarbon ions. The dependency of grain size and phase purity on the process parameters and boron incorporation was investigated. Due to boron incorporation the grown nc diamond films show a lower intrinsic compressive stress, which is due to a compensation effect between the boron doping-induced tensile stress and the ion subplantation-induced compressive stress. The nc films show strongly improved electron emission properties. Low-field electron emission and high emission current have been achieved from the films consisting of nanosized diamond grains, showing a long-term stability.