A study of the Al-Mg-B ternary phase diagram
Abstract
The Al(x)Mg(1-x)B2 solid solution was studied at temperatures of 900, 1000, 1200 and 1400 C using X-ray diffraction. From the obtained data, isothermal sections at 1000, 1200 and 1400 deg C have been proposed for the Al-Mg-B ternary system. Based on these results there exists an equilibrium between Al and AlMgB14 at temperatures above 1000 deg C. Entnommen aus <a_href="http://www.fiz-technik.de/db/b_tema.htm" target="_blank">TEMA</a>