Shot peening of ceramics: Damage or benefit?

 
: Pfeiffer, W.; Frey, T.

Ceramic forum international : CFI. Berichte der Deutschen Keramischen Gesellschaft 79 (2002), No.4, pp.E25-E28
ISSN: 0173-9913
English
Journal Article
Fraunhofer IWM ()
ceramic; shot-peening; strength; residual stress; load capacity; wear; silicon nitride; alumina

Abstract
Non-transformation toughened ceramics show the typical brittle material behavior of failure before deformation at room temperature. Thus, strengthening of ceramics due to deformation induced compressive residual stresses has been thought to be not possible. Nevertheless, preliminary investigations had shown that, using ceramic-specific parameters, shot peening can introduce high compressive residual stresses into the near-surface of silicon nitride and improve the load capacity. The aim of the presented investigation was to improve the shot peening conditions in order to extend the increase of load capacity while maintaining the surface integrity. The materials investigated where alumina and silicon nitride, the properties determined where residual stresses, load capacity and topography. The results show that high compressive residual stresses in the GPa-range can be introduced in silicon nitride and alumina which may boost the load capacity of the near surface layers by a factor of up to 9. Only little effect on the surface integrity could be obtained.

: http://publica.fraunhofer.de/documents/B-83041.html